韩国LG一级代理，价格电议。
特性： 含紫外线稳定剂，高粘，过滤380nm以下紫外线应用： 片材，光学透镜，薄膜，家电 1302-05 测试项目 测试方法 单位 数值 Melt Flow Rate(300℃/1.2kg) ASTM D1238 g/10min 5 Density ASTM D792 1.2 Mold Shinkage ASTM D955 mm/mm 0.005-0.007 Wate Absoption@24hs,23℃ ASTM D570 % 0.15 @equilibium,50%RH,23℃ ASTM D570 % 0.32 Refactive index,no ASTM D542 1.586 Light Tansmittance ASTM D1003 % 89 Haze ASTM D1003 % 0.7-1.5 Deflection Tempeatue Unde Load(DTUL)@4mm ASTM D648 ℃ @66 psi(0.45MPa),annealed ASTM D648 ℃ 146 @264 psi(1.8MPa),annealed ASTM D648 ℃ 143 @264 psi(1.8MPa),unannealed ASTM D648 ℃ 132 Vicat Softening Point,50℃/h,50N Load ASTM D1525 ℃ 151 Coefficient of Linea Themal Expansion,@-40 to 82℃ ASTM D696 mm/mm/℃ 68×10-6
Tensile Yield Stength ASTM D638 Mpa 60 Ultimate Tensile Stength ASTM D638 Mpa 72 Elongation at Yield ASTM D638 % 6 Elongation at Beak ASTM D638 % 150 Tensile Modulus ASTM D638 Mpa 2410 Flexual Stength ASTM D790 Mpa 96 Flexual Modulus ASTM D790 Mpa 2410 Notched Izod Impact @23℃ ASTM D256 J/m 950 Unnotched Izod Impact @23℃ ASTM D256 No beak Instumented Dat Impact,Total Enegy @23℃ ASTM D3763 J 94 Rockwell Hadness ASTM D785 M Scale 74 Tabe Abasion Resistance (△Haze) ASTM D1044 % 45
UL-94 @0.5mm ASTM D635 V-2 UL-94 @1.6mm ASTM D635 V-2 UL-94 @2.5-2.7mm ASTM D635 V-2 UL-94 @3.0mm ASTM D635 V-2 Limiting Oxygen Index ASTM D2863 % 26 Ball Indentation Tempeatue IEC598-1 ℃ >125 Aveage Extent of Buning ASTM D635 mm 25
GWT2.0mm,5second IEC695-2-1 ℃ 850 Compaative Tacking Index@2.0mm IEC112 V 250 Dielectic Stength ASTM D149 kv/mm 17 Eielectic Constant @60Hz ASTM D150 3 Dissipation Facto@60Hz ASTM D150 0.001 Volume Resistivity @23℃,dy ASTM D257 Ω-cm 2.0×1017